This product is made of weaving continuous filaments (without breaking), then the fabric is passed through high-temperature ovens to burn organic elements and reduce the weight (density). After this heat treatment, the color of the fiberglass fabric is changed to brown and will not cause any smoke during use.
Due to the texture and application of simple fiberglass fabric, it’s not very different, but it is especially used for applications that should not be released.
|Testing Method||8HS Satin||Weave||1|
|ISO 4602||ECG 75 1/3||EC9 66 1×3||Warp||Yarn||2|
|ISO 4602||ECG 75 1/3||EC9 66 1×1||Weft||(Tex)||3|
|ASTM-D-3774||40 inch||100 cm||Width||4|
|48 inch||150 cm|
|_||Caramelized (heat treatment)||TREATMENT||5|
|ASTM-D-3776||19.5 OZ/YD2||660 g/m2||Cloth Weight||6|
|ASTM-D-1777||0.028 inch||0.70±0.5 mm||Total Thickness||7|
|ASTM-D-3775||40 per inch||16 per cm||Warp||Thread Count||8|
|38 per inch||15 per cm||Weft|
|ASTM-D-5035||733 lbs/inch||6600 N/5cm||Warp||TENSILE STRENGTH (Min)||9|
|555 lbs/inch||5000 N/5cm||Weft|
|_||Up to 550°C||Service Temperature||10|